The temperature of large roll galvanized wire should be controlled at 30 to 50℃ during electroplating. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used. Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Hot dip galvanizing is in the hot melt zinc liquid dip plating, production speed, thick but uneven coating, the market allows the low thickness of 45 microns, up to 300 microns above. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.

6, passivation to remove hydrogen parts should be passivation after the removal of hydrogen, passivation before the application of 1%H2SO4 or 1% hydrochloric acid activation 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.

In order to remove the photosynovium and oxide remaining on the surface of galvanized iron wire after drawing or heat treatment, it is necessary to do the surface treatment of galvanized steel wire before plating. The common surface of low carbon steel wire is the light synovium or oxide of animal or vegetable oil; Medium and high carbon steel in addition to contain animal or vegetable oil components.

With the development of mining industry, pig iron classification in Our country has been very extensive, can satisfy the demand of machinery industry. In general, iron used to produce large coils of galvanized wire can be divided into two classes. A metal produced directly from iron ore and iron smelting, consisting of iron oxide, silicon dioxide, and other miscellaneous stones. When this ore is specially refined into metal iron, carbon, silicon, manganese, and other elements are mixed in, so that the refined material is called general pig iron, is also for the initial grade of the material.

Advantages: The cost of hot dip galvanized rust prevention is lower than that of other paint coating. In suburban environment, the standard hot-dip galvanized rust prevention thickness can adhere to more than 50 years without repair. In urban or offshore areas, the standard hot-dip galvanized rust protection layer can last 20 years without repair. Galvanized layer and steel is a metallurgical connection, into a part of the steel surface, so the durability of the coating is more reliable.