Environmental factors should be considered when choosing the thickness of galvanized layer. Galvanized wire in galvanized, pay attention to the above problems, can be well galvanized, to ensure the quality of galvanized wire. Galvanized methods are mainly divided into two types, one is hot dip galvanizing method, the other is electric galvanizing method. This paper mainly introduces the method of galvanizing. Electrogalvanizing is an electrolyte used for galvanizing.

Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Hot dip galvanizing is dipped in zinc liquid melted by heating. It has fast production speed, thick but uneven coating. The market thickness is 45g and can reach more than 300g. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.

If it is not packaged, then a car of blade thorn rope can not be loaded with many pieces, and it is also relatively occupied and easy to lose in the transportation process. The number of the packed blade thorn rope is 50 bundles, and the volume is reduced after hydraulic compression so that it is more convenient to load and unload, and the forklift can easily load and unload. Under normal circumstances, when exporting, the blade thorn rope will be packaged and sold, so that the volume occupied in the container is relatively small, which can be easily placed and will not occupy much place.

Every galvanized wire production into the peak season of the industry, the road to the factory will from time to time see transportation wire and container container vehicles, as well as galvanized bright silk short-distance transportation trucks, led to the utilization of labor in the surrounding countryside, solved the employment problem of most people. Galvanized wire is divided into hot plating wire and cold plating wire.

The derusting steel parts are immersed in the melted zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to achieve the purpose of anti-corrosion. The surface of galvanized wire coating can see whether the quality of galvanized wire is good or not. If the strength of zinc attached to the wire is very poor, then this galvanized wire do not buy, because this galvanized wire must be poor galvanized wire.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.