To remove surface active substances by matting with activated carbon. Or filtration to make the foam less stable, which are effective measures; Other measures should also be taken to reduce the amount of surface-active substances brought in to Z. The electroplating speed can be significantly reduced by the introduction of organic matter. Although the chemical formula is conducive to a high deposition rate, the coating thickness cannot meet the requirements after the organic matter is loaded, so activated carbon can be used to treat the tank.
The main customers of the barbed rope factory are still targeted at the farm and plantation customers for sales, because the demand for barbed rope is often very large.
The main raw materials of blade barbed wire are galvanized wire and galvanized sheet. Because the price of galvanized sheet is more expensive than galvanized wire, it is directly reflected in the price of blade barbed wire. There is also the difference in processing technology also leads to the difference in the price of the blade. The traditional barbed rope is made of mechanical wringing, which has a relatively small amount of labor and high production efficiency. However, the blade barbed rope is processed manually after secondary mechanical processing. So whether from the labor force or from the production efficiency also said that there is a large gap. These factors lead to the price of the blade barbed rope is more expensive.
Usually, there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment is easier to rust than dry environment, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the customized corrosion of hexagonal guardrail and extend the service life of the product.
Razor blade barbed rope has been widely used in military sites, prisons, government agencies, banks in the world. The walls of living quarters, private homes, villas, fences, doors and Windows, highways, railway guardrail and border lines and other protection and security.
As we all know, the use of hexagonal net for protection can protect the natural environment while protecting the bridge, which can not only green the ecological environment, but also prevent soil erosion.
Galvanized iron wire is widely used in construction, handicrafts, wire mesh, highway guardrail, product packaging and daily civilian and other fields.
The anticorrosion of these raw materials is very different, and the use of life is not the same. Niu LAN net cold galvanized, also known as electroplating, galvanized quantity is very little, rust in rain, but the price is cheap, the use of life in 5-6 years. Hot dip galvanizing (low zinc and high zinc) on the amount of zinc in 60 grams to 400 grams, the service life is about 20-60 years, corrosion resistance is general.
Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.
Large roll galvanized wire is divided into hot dip galvanized and cold galvanized two kinds, hot dip galvanized color is dark, consumption of zinc metal, and matrix metal formation of infiltration layer, good corrosion resistance, hot dip galvanized can be maintained for decades in outdoor environment. Cold galvanized production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.
After passivation treatment of galvanized layer, a layer of bright old and beautiful color passivation film can be generated, which can significantly improve its protective performance. There are many kinds of galvanized solution, which can be divided into cyanide plating solution and cyanide plating solution. Cyanide galvanizing solution has good dispersion and covering ability, coating crystallization is smooth and fine, simple operation, wide application range, has been used in production for a long time.
Continuous production does not need heating, but needs cooling. Cooling can be in the groove side row thin wall plastic pipe, through the flow of tap water cooling, can also be used as a titanium pipe temperature control device. In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc.
Many customers are in great need of galvanized barbed rope when they decide to purchase it, and the barbed rope specification determines the length of the later installation.
Now the production of stainless steel blade barbed rope unless it is a specially customized model, under normal circumstances are the use of a knife length of 22mm mold production, that is, we usually say bto-22 type. It’s not necessarily the case that there are specifications from 11mm to 65mm. Unless the customer insists on customizing the required length, the barbed rope manufacturer produces bto-22 stainless steel blade barbed rope.
The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.