The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.

In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized process, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well.

Cold drawing wire is a metal cold processing, with wire rod as raw material, that is, the mouth of the steel bar. Cold drawing wire is a product produced by a series of processes such as shell stripping, which is a common wire. In the development and production of metal materials, cold drawing wire is a very common material, its performance is good, the range of use is very wide, manufacturers in processing are the use of cold processing to produce.

Galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire is widely used. Electroplating temperature should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.