For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by customers. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this thing is more important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized silk, the weight can reach 300kg/ roll or 800kg/ roll.

Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.

Stainless steel barbed wire is mainly used in the place near the sea more, wet salty air for metal corrosion is particularly serious, and the selection of stainless steel barbed wire is in order to prevent corrosion.

High quality galvanized wire in general, the zinc layer attached to the surface of the wire is relatively thick, so when we buy galvanized wire, as long as we look at the thickness of the zinc layer machine, we can generally judge whether the quality of galvanized wire is high quality.

2, mesh, mesh also directly affect the price of stone cage net

Widely used in practice, iron wire also has certain harm, simple rust and corrosion, so we can generally use galvanized method to prevent product corrosion. Together in addition to this method, metal commonly used treatment methods and phosphating treatment, oxidation treatment, etc. Metal phosphating treatment: iron and steel products to remove oil, rust, into the specific composition of the salt solution soak, you can form a layer of water soluble salt film on the surface of the metal, this process is called phosphating treatment.

Galvanized wire is processed from low carbon steel wire rod, after drawing forming, pickling rust removal, high temperature annealing, cooling and other processes. Galvanized wire is widely used. Electroplating temperature should be controlled at 30 to 50℃. Because the chloride ions in the bath are very corrosive, quartz glass heaters are generally used.

Purpose of galvanized hexagonal net: building wall fixed, heat preservation, heat insulation; Power plant tied pipe, boiler warm; Anti-freezing, residential protection, landscaping protection; Raising chickens and ducks, isolating chicken and duck houses, to protect poultry; To protect and support seawalls, hillsides, roads and Bridges and other waterworks.