There are too many fake things on the market now, so shoppers should learn how to distinguish the quality of galvanized wire, the right to protect their consumers’ rights and interests. Galvanizing process of galvanized wire products is a very effective metal anticorrosion method, and it is also widely used in other industrial fields. After galvanizing, iron wire is commonly used in metal structure equipment of various industries.

With the improvement of people’s living standards now, many families are keeping some small pets, these small pets also need a stable nest, pet cage has become a more important choice of people, each pet habits and living habits will choose to adapt to the cage.

Cold drawing wire is a metal cold processing, with wire rod as raw material, that is, the mouth of the steel bar. Cold drawing wire is a product produced by a series of processes such as shell stripping, which is a common wire. In the development and production of metal materials, cold drawing wire is a very common material, its performance is good, the range of use is very wide, manufacturers in processing are the use of cold processing to produce.

The invention technology is used to put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and plays an important measure to stabilize the PH value within a numerical range, and also facilitate the filter filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.

With the improvement of people’s living standards, now many families are raising some small pets, these small pets also need a safe nest, pet cage has become an important choice of people, each pet’s habits and living habits will choose to adapt to the cage.

A. When the thickness of the plating is 3-4 mm, the zinc adhesion should be less than 460g/m, that is, the average thickness of the zinc layer is not less than 65 microns.

The formation process of hot dip galvanized layer is between the iron matrix and the outside of the pure zinc layer, the formation of iron-zinc alloy process, the workpiece surface in hot dip plating when the formation of iron-zinc alloy layer, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc liquid, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the attraction between the atoms is relatively small.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.