Wire mesh welding after galvanized is through the end of the welding and then the cold company to make wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot galvanized. After the first galvanized welding is to change the wire mesh, after the end of welding can see the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the appearance is smooth, and the cost of the first welding after plating is higher, not easy to rust.

The wire diameter of raw materials used in different types of barbed rope is also very different, but in the production and processing process of barbed rope need to know the amount of use.

In order to orchard special electric galvanized shaft wire in alluvial surface to partially remove the surface film layer, surface impurity and other shortcomings can be found and solved according to the basic technology; Excessive foam is caused by soap and soapable surface active substances such as human fat into the tank. A moderate rate of foam production would be fine. The large amount of fine homogeneous particles in the tank can stabilize the foam layer, but the accumulation of too much solid particles will cause explosion.

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

(2) Packing and binding galvanized shaft wire order notes: ① the galvanized iron wire shall not be damaged when the tightening. (2) Stop the use of more than two strands of galvanized iron wire around the operation method. ③ The diameter of galvanized wire for pulling should not be less than 4mm, and the diameter of galvanized wire for binding should not be less than 2.6mm. (4) Galvanized iron wire shall not be used as waist hoop down reinforcement, usually not used as a whole binding. Warehouse galvanized wire is mainly used to block and distinguish the function of the area, warehouse galvanized wire is one of the primary use of galvanized wire, warehouse galvanized wire primary layout features are as follows: layout: Column mesh frame, column to choose square steel pipe, galvanized wire frame is also a small square pipe as the data, column and mesh frame corresponding direction are welded connecting ear piece (flat iron), column and mesh frame through the connection of the ear piece bolt fixed, column bottom welding plate, column bottom plate through expansion bolts and fixed on the ground.

Different from common zinc barbed rope, high zinc barbed rope surface zinc content is very high can reach 6-8 times of the former, so there is a great advantage in the service life, ordinary products begin to corrosion three to five years while the latter will take longer to change. Stainless steel barbed rope is in material protection so durability is also better, these two products are long service life, but in terms of high price.