The first is the cost of raw materials galvanized sheet and galvanized wire, some specifications and waste calculation and so on. Then there is the cost of mechanical processing process and manual processing process. Finally, there is the cost of packing and shipping. In recent years, due to the rapid development of thorn rope manufacturers, so the profit margin of blade thorn rope is not particularly broad.

Broken wire is the iron bright wire, fire wire, galvanized wire, plastic coated wire, paint wire and other metal wire, wire factory according to customer requirements for straightening after sizing cut, has the characteristics of easy transportation, easy to use, widely used in the construction industry, handicrafts, daily civilian and other fields. No limit on length, packing as required. Annealing wire also known as black oiled wire, black annealing wire, fire wire, black iron wire. Compared with cold drawing, black annealed wire is more economical as raw material for nails.

The formation process of hot dip galvanized layer is between the iron matrix and the outside of the pure zinc layer, the formation of iron-zinc alloy process, the workpiece surface in hot dip plating when the formation of iron-zinc alloy layer, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc liquid, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the attraction between the atoms is relatively small.

Hexagonal mesh is also known as twisted mesh, insulation mesh, soft edge mesh. It is made of a single mesh reel. The mesh, mesh, galvanized and PVC coated properties are the same as the cage. This product can be different shapes, sizes of the stone into the alloy net to form a flexible whole, can be lifted, cars, shipping to the L place, the alloy net connected into a larger whole, the construction of throwing convenient, fast, good economic performance.

Wire factory introduction annealing wire is widely used mainly because it has good elasticity and flexibility, in the process of annealing can be very good control of its soft and hard degree, it is mainly made of iron wire, more often used in the construction industry tied wire use. In the production of annealing wire will be processed according to the performance of the material, according to the demand for different degree of hardness of its soft change, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.

Because the coastline is generally erected for protection, but often because of environmental factors lead to serious corrosion of the barbed rope lost its function. Stainless steel barbed rope is specially set up to prevent corrosion. Stainless steel barbed rope because the environmental requirements are not very high can be very good protection itself will not have a problem to extend the use of life, so that you can ensure safety.

The welding core is the metal core of the electrode. In order to ensure the quality of the weld, there are strict regulations on the content of various metal elements in the weld core. In particular, there are strict restrictions on harmful impurities (such as sulfur and phosphorus), and the quality of the weld core metal should be better than that of the base metal. Arc welding cannot be carried out on a smooth rod without a coating. This is because the arc stability is very poor, splashing is very large, and the weld is not well formed. After long-term practice, it is gradually found that the performance of the electrode is greatly improved by coating the welding core with some mineral raw materials (i.e. electrode coating). (1) Ensure stable arc combustion, so that the welding process is normal. (2) Using the gas produced after the drug skin reaction, protect the arc and the molten pool, prevent the harmful gases in the air (such as nitrogen, oxygen, etc.) from invading the molten pool, such as these gases will cause cracks and pores in the welding material, so that the welding can not achieve the ideal effect. (3) After the drug skin is melted, slag is formed, which covers the weld surface to protect the weld metal, make the weld metal slowly cool, help the gas escape, prevent the generation of pores, and improve the structure and performance of the weld. (4) After melting, various metallurgical reactions will be carried out, such as deoxygenation, sulfur removal, phosphorus removal, etc., so as to improve weld quality and reduce alloying element burning loss.

Stainless steel barbed wire is often used in various engineering projects because of its good anti-corrosion ability, but it is difficult for ordinary families to accept because of its relatively high price. So what material of barbed rope anticorrosion ability is better?

After the optimization of the process, mass production of 0.80mm electro galvanized steel wire electro galvanized zinc layer quality is controlled within 80 ~ 90g/m2, zinc layer quality dispersion is very small; The results show that the average weight of zinc layer is 14.5g/m2, the loss of zinc layer is less than 5%, and the tensile strength of steel wire is 2300 ~ 2500MPa. It not only effectively controls the quality of zinc layer of raw steel wire, but also reduces unnecessary waste and production cost.