In the process of composite plating, it is necessary to stir the plating solution to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized and other processes, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire.

Welding electrode has a wide range of applications, can realize a variety of materials, a variety of profiles and a variety of joint forms of welding.

In order to pack and bind galvanized wire in the surface of the sedimentary layer to local removal of surface film, surface inclusion and other defects can be found and treated by conventional technology; Excess foam is formed when soap and surfactants such as saponified fats are brought into the tank. Moderate rates of foam formation may be harmless. Small, homogeneous particles of large denier present in the bath can stabilize the foam layer. Use activated carbon mat to remove surface active substance. Or through filtration to make the foam is not too stable, which are effective measures; Other measures should also be taken to reduce the amount of surfactant introduced. The electroplating speed can be obviously reduced by the addition of organic matter. Although chemical formulations facilitate high deposition rates, the deposition of organic matter does not meet the requirements of coating thickness, so activated carbon can be used to treat the bath.

Hot dip galvanizing is in the hot melt zinc liquid dip plating, production speed, thick but uneven coating, the market allows the low thickness of 45 microns, up to 300 microns above. It is dark in color, consumes more zinc metal, forms infiltration layer with base metal, and has good corrosion resistance. Hot dip galvanizing can be maintained for decades in outdoor environment.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, The softness is also very uniform, the color is consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding hanger, reprocessing industry, etc.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

Breeding cattle and sheep with barbed rope effect or better, because the advantages of barbed rope more. Then the barbed rope used for animal husbandry effect is good?

2, the production and installation is simple and fast, the use of patented friction connection or special connection accessories for installation, greatly improve the installation efficiency.