Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Pet cage has many types, and selective is bigger, pet cages are generally made of wire, with better coarse, then at the bottom with a wheel base, such a simple pet basket was made, in the wheel at the bottom of the mount is for the convenience of the mobile, a pet cages should also adapt to the location of the production in addition to a door, Convenient in pet feeding when more convenient.

Razor blade barbed rope has been widely used in military sites, prisons, government agencies, banks in the world. The walls of living quarters, private homes, villas, fences, doors and Windows, highways, railway guardrail and border lines and other protection and security.

This oxide film has greater elasticity and lubricity, does not affect the accuracy of parts. Therefore, the parts of precision instruments and optical instruments, spring steel, thin steel sheet, fine steel wire and so on are commonly bluing treatment. The commonly used galvanizing treatment of large roll galvanized wire is equivalent to forming a protective layer on the surface of the iron wire. The commonly used methods are hot dip galvanizing, hot spray plating, vacuum plating and so on. Different methods have corresponding characteristics.

Hot dip galvanizing, also known as hot dip zinc and hot dip galvanizing, is an effective way of metal corrosion prevention, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel member is attached with zinc layer, so as to play the purpose of anticorrosion.

In order to orchard special electric galvanized shaft wire in alluvial surface to partially remove the surface film layer, surface impurity and other shortcomings can be found and solved according to the basic technology; Excessive foam is caused by soap and soapable surface active substances such as human fat into the tank. A moderate rate of foam production would be fine. The large amount of fine homogeneous particles in the tank can stabilize the foam layer, but the accumulation of too much solid particles will cause explosion.

Cold wire drawing is a kind of cold processing of metal, that is, we often say reinforcement. Cold drawing process is not messy, cold drawing price based on the quality of cold drawing dividends of different levels, cold drawing production is also a variety of different procedures. The main factor affecting the strength of cold drawing wire is raw materials, which are closely related to the raw materials, strength and diameter of raw materials, and the better the quality of cold drawing wire, the more messy the production process.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.

2. Eliminate caked zinc residue on zinc liquid surface