If the surface of galvanized wire is black and the galvanized layer is thin and uneven, the galvanized wire is partly because the inventory storage time is longer, but also because the production technical requirements of galvanized wire do not meet the standard and lead to the quality problems of galvanized wire. According to the use of galvanized wire is different, galvanized wire has soft and hard, then the galvanized wire used for binding requires the flexibility of galvanized wire is better, the flexibility of galvanized wire is good, and it can be easy for workers to operate.

Some customers pay more attention to the quality problem, so they pay more attention to the service life. The barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

In order to improve the corrosion resistance of steel pipe, the general steel pipe is galvanized. Galvanized steel pipe is divided into hot dip galvanized and electric galvanized. The layer of hot dip galvanized is thick, the cost of electric galvanized is low, and the surface is not very smooth. Used for steel blowing oxygen pipe, generally with small diameter welded steel pipe, specifications from 3/8-2 inches of eight. Made of 08, 10, 15, 20 or 195-Q235 steel strip, in order to prevent corrosion, some should be aluminized.

Different supports are used for different installation environments. In the past, the blade barbed wire was not easy to fix, and the installation environment was often steep. Therefore, special tools must be used to fix the blade barbed wire to prevent it from being improperly installed.

Out-of-line annealing means that the recrystallization annealing of hot or cold rolled steel plate is carried out in the bottom type annealing furnace or cover type annealing furnace before entering the hot plating wire line, so that there is no annealing process in the galvanized line. The steel plate must maintain a clean active surface of pure iron, free of oxides and other dirt, before hot dip galvanizing. In this method, the annealed surface oxide sheet is first removed by pickling method, and then coated with a layer of zinc chloride or a mixture of ammonium chloride and zinc chloride solvent for protection, so as to prevent the plate from being oxidized again.

6, according to the wire diameter thickness to adjust zinc dipping time. Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is the length of the distance between the lead screw on the zinc pot and the ceramic sinking roll. The zinc dipping time of coarse wire diameter should be long, and the zinc dipping time of fine wire diameter should be short.

There is in place to use, the blade thorn rope is commonly border, installation and use of the fence, and prisons, and galvanized barbed wire is in the orchard, fence livestock and so on the installation of large area, although the use of relatively large, but not as good as the use of blade thorn rope and high grade, so this is also the main reason for the price is quite high. Finally, the general installation site of the blade barbed rope for the protection level requirements are relatively high, so the quality requirements for the product is also relatively high, but the ordinary galvanized barbed rope because of the requirements in the installation site is more casual, which is also for the processing process for the quality requirements are relatively low.

First of all, we need to pay attention to the material of the barbed wire, because the galvanized barbed wire itself includes cold plating and hot plating. The properties and prices of the two are obviously different, and it is easy to be confused by a little negligence.

Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.