Electric galvanized wire direct selling is in the plating tank through the current one-way to gradually zinc plating on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanizing shiny white.

The main raw materials of blade barbed wire are galvanized wire and galvanized sheet. Because the price of galvanized sheet is more expensive than galvanized wire, it is directly reflected in the price of blade barbed wire. There is also the difference in processing technology also leads to the difference in the price of the blade. The traditional barbed rope is made of mechanical wringing, which has a relatively small amount of labor and high production efficiency. However, the blade barbed rope is processed manually after secondary mechanical processing. So whether from the labor force or from the production efficiency also said that there is a large gap. These factors lead to the price of the blade barbed rope is more expensive.

Use in daily life does not need to carry out maintenance and maintenance, save a lot of time, but also save maintenance and maintenance costs. The annealed wire has good stability and corrosion resistance, which greatly prolongs its service life. There are many kinds, which can be selected according to different uses. The device for making anneal wire is simple, which improves the utilization rate of the device. The material properties of annealed wire can meet different processing requirements.

Annealing wire is widely used mainly because it has a good elasticity and flexibility, in the annealing process can be a good control of its hardness and softness, it is mainly made of iron wire, more commonly used in the construction industry tie wire use. When the wire factory is in production, the annealing wire will be processed according to the performance of the material, and its hardness will be changed according to the different demand, which can make it have more advantages, reduce the consumption of metal and reduce the cost of production.

Wire factory introduction annealing wire is widely used mainly because it has good elasticity and flexibility, in the process of annealing can be very good control of its soft and hard degree, it is mainly made of iron wire, more often used in the construction industry tied wire use. In the production of annealing wire will be processed according to the performance of the material, according to the demand for different degree of hardness of its soft change, can make it has more advantages, can reduce the consumption of metal, reduce the cost of production.

Cold plating is a physical treatment method, the zinc is simple and uneven, the amount of zinc is also less than in the corrosion and rust prevention and chemical disposal of hot plating; The amount of hot zinc plating is relatively thick, the surface of the disposal is flat on average, and it is not easy to fall off. A layer of alloy composed of zinc and metal has very strong oxidation ability, and there is a layer of pure zinc on the outside of this layer of alloy, which is why hot plating is thicker and stronger than cold plating. Under the condition of high degree of natural recovery, galvanized hook net can play a very good maintenance effect on the environment, it is not afraid of wind and rain, it is the battle machine in the hook net, much stronger than the dip plastic hook net.

For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by customers. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this thing is more important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized silk, the weight can reach 300kg/ roll or 800kg/ roll.

There are two varieties of steel grid plate is pressure welded steel grid plate and pressure lock steel grid plate, in many people’s eyes, these two products belong to the same variety, in fact, there are still great differences between them in many places.

There are various specifications of barbed rope, which can be divided into two categories: ordinary barbed rope and blade barbed rope.