The advantages of hexagonal net to do jet hanging net, the first is that the processing speed is fast, the cost is low, and it is very good to roll out when it is open because of the edge. Common specifications: 12 cm x15 cm (11cm x11 cm) 11 cm x15 cm (10 cm x10 cm) 10 cm x12 cm (9 cm x9 cm) 9 cm x13 cm (9 cm x9 cm) 8 cm x10 cm (7 cm x7 cm) common wire: 1.3mm 1.4mm 1.5mm 1.6mm 1.7mm 1.8mm 2.0mm 2.3mm 2.5mm Commonly used materials: galvanized wire hot dip galvanized wire to wire drawn zinc aluminum alloy plastic coated wire stainless steel wire.

The application range of positive and negative twisted barbed wire is also very wide. It is a good choice for purchasing barbed wire. So what are the advantages of positive and negative twisted barbed wire compared with other barbed wires? The following  barbed wire factory will introduce the positive and negative twisted wire in detail. Three advantages of rope

The production process is to roll the hot metal billet into 5mm thick steel, and then put it into the wire drawing device, draw into different diameters of the line and gradually reduce the aperture of the wire drawing disk. Production process through cooling, annealing, coating and other processing technology, and then made into a variety of different specifications of galvanized wire. Galvanized wire production because of simple process, wide application, early development. Galvanized wire or steel wire is a cold working product of steel wire, and the material used is generally low carbon steel or stainless steel.

The formation process of hot dip galvanized layer is between the iron matrix and the outside of the pure zinc layer, the formation of iron-zinc alloy process, the workpiece surface in hot dip plating when the formation of iron-zinc alloy layer, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc liquid, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the attraction between the atoms is relatively small.

Hot drawing is the heating before the wire enters the die hole, mainly used for high melting point wire drawing; The temperature drawing is carried out by heating the heater to the range of temperature, mainly used for galvanized steel wire, difficult to deform drawing.

At present, there are two processing methods of blade stabbing rope. One is to make it into a spiral shape, and then make a clip treatment. It is not only our common spiral blade stabbing rope, but also a single spiral blade stabbing rope without clip, but even a single helix can not stretch it to a relatively straight. This is mainly because the blade barbed rope is wrapped and wound at the same time, so it can only be spiral.

The external environment has a great influence on the storage of cold drawn wire. Especially during the rainy season, special attention should be paid to the air humidity of workshops and warehouses. It is recommended to use moisture test paper with a value between 8 and 10. If the PH value is high, attention should be paid to the corrosion of the internal cold drawing wire. Cold drawing wire in normal environment storage for two years no problem, cold drawing wire will not be corroded. However, it is necessary to place the coil gently during the handling process to avoid the winding position leading to the cable is not smooth.

For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by the customer. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this is very important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized wire, the weight can reach 300kg/ roll or 800kg/ roll.

Now more and more people are buying the barbed rope, but there are often a lot of people do not know the specifications of the blade barbed rope when they buy, here is to introduce the specific characteristics of the blade barbed rope.

The application of electric welding mesh is more widely, at present, it has replaced the use of other parts of the screen, the cost of electric welding mesh is low, the production speed is very fast, so it is very popular. The treatment required before galvanized welding mesh is recrystallization annealing, because the welding mesh must maintain an oxide and no other impurities of pure iron active surface, if you can’t keep its surface clean will lead to poor galvanized effect, galvanized layer and iron material is not tightly combined, so this step is necessary.

In order to orchard special electric galvanized shaft wire in alluvial surface to partially remove the surface film layer, surface impurity and other shortcomings can be found and solved according to the basic technology; Excessive foam is caused by soap and soapable surface active substances such as human fat into the tank. A moderate rate of foam production would be fine. The large amount of fine homogeneous particles in the tank can stabilize the foam layer, but the accumulation of too much solid particles will cause explosion.