Annealed wire is a soft iron wire made of low carbon steel cold drawing, heating, constant temperature, heat preservation and other processes. The composition of iron wire varies according to its use. It contains iron, cobalt, nickel, copper, carbon, zinc, and other elements. The hot metal billet rolled into 6.5mm thick steel bar is the wire rod, and then put it into the wire drawing device into a different diameter of the line, and gradually reduce the aperture of the wire tray, cooling, annealing, plating and other processing technology made of various specifications of iron wire.

Barbed rope is to use iron wire, through winding machine, through a variety of weaving technology, wound in the main line (stranded) made of isolation protection net. There are three ways to twist the barbed rope, as detailed below.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

5, the concentration of plating aid can not be too high, which is a factor that can not be ignored to reduce zinc consumption. The concentration of plating aid should not be too high. The galvanized line must be added with ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution should be controlled within the range of 50~80g/L. If ammonium chloride or zinc chloride is arbitrarily added without the results of laboratory analysis, it should be criticized and educated, and economic treatment should be given if necessary.

Advantages: The cost of hot dip galvanized rust prevention is lower than that of other paint coating. In suburban environment, the standard hot-dip galvanized rust prevention thickness can adhere to more than 50 years without repair. In urban or offshore areas, the standard hot-dip galvanized rust protection layer can last 20 years without repair. Galvanized layer and steel is a metallurgical connection, into a part of the steel surface, so the durability of the coating is more reliable.