The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.

Large roll galvanized wire welding net is made of high quality galvanized wire welding net, wire through the current, after mutual melting, strong connection point, and the formation of metal mesh. In the use of galvanized iron wire to find the thickness and soft and hard to the size of flowers, weight and softness corresponding to the degree, too soft florets to use fine wire, and heavy flowers, flowers with thick stems to use thick wire.

3. Put zinc block into the plating aid pool regularly, so that the bivalent iron in the plating aid becomes trivalent iron, and it is an important measure to stabilize the PH value in a numerical range. At the same time, it is convenient for the filter to filter out the trivalent iron ions in the plating aid; Ferric ion is controlled between 0.3 and 1.0g/L; When hydrogen is not released in the plating aid, the zinc block is continued. It is an effective measure to reduce zinc slag, improve the fluidity of zinc liquid and reduce the thickness of zinc layer to play the role of plating aid filter.

Bridge protection system generally do not need to be specially installed special drainage system, the use of hexagonal mesh made of gabion mesh box, the inside of the filler are selected stones, these stones are not easy to wear, and between the stones and stones will retain some gaps, so it is very good to meet the drainage requirements.

The amount of zinc on the surface of high zinc barbed rope is about 5 times that of general zinc barbed rope, thus greatly prolonging the time of rust resistance. In the appearance of the two products are silver white and metal texture is better, for the distinction between the two products is more difficult to distinguish if it is a layman, but for long-term work of professionals can be separated from the two at a glance.