Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Solid particles or excessive foreign metal impurities in the electroplating solution can cause such problems. Solution: If the coating of large galvanized wire is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

Hook flower net is made of silk hook, the mesh is uniform, flat net surface, beautiful generous net width, wire diameter is thick, not easy to corrode long life, weaving succinct, beautiful and useful. Widely used for raising chickens, ducks, geese, rabbits and zoo enclosures. Mechanical equipment protection, highway guardrail, sports venues fence, road beautification belt protection network. After the screen is made into a box-like container, it can be used to maintain and support the seawall, hillside, road and bridge, reservoir and other civil engineering.

The corrosion or discoloration of galvanized iron wire in the atmosphere caused by oxygen, moisture and other pollution impurities is called rust or rust. After galvanized iron wire rusting, it will affect the appearance quality, seriously affect the use, and even cause scrap, so galvanized iron wire must be properly kept and pay attention to rust prevention.

It is precisely because of the advantages of electric welding mesh (explanation: can overwhelm the favorable situation of the other side), the electric welding mesh in the market is widely used in urban roads, real estate, development zones, residential areas, gardens and all kinds of enterprises and institutions of decoration beautification and security protection works. Stainless steel wire mesh is one of stainless steel wire mesh products.

2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.

Poor pretreatment before electroplating; Bath temperature is too low; Poor quality additives or excessive additives and organic impurities can cause poor bonding. The quality of the additive also has an effect on coating foaming. Some additives react incompletely during synthesis and continue to polymerize during long-term storage or use. The additive tends to distort the lattice and create stress, causing the coating to blister.

1, zinc pot workers to resolutely do duty and responsibility. Do not leave the post without permission, always observe the change of steel wire galvanized layer, and according to the analysis of the results, master asbestos block gap friction need how long to press, replace the pressing face; Adjust the working face; Until the four faces of the asbestos block are used up, maintenance workers continue to use it after repair when necessary to reduce the consumption of asbestos block.