Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

The main customers of the thorn rope factory are still targeted at farms and plantations, because the demand for thorn rope is often very large.

When the coating of large galvanized wire is blistered in the process of galvanizing, the bath temperature should be checked first. If the bath temperature is not low, and then strengthen the removal of oil before plating, to prevent the base metal in acid corrosion. If you pay attention to these problems, the bubbling phenomenon still exists, it should pay attention to the dosage and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, to reduce the content of additives, observe whether the bubbling phenomenon is improved. If there is no improvement, check whether the additive has been stored for too long or whether it contains too many impurities.

With the technique of preventing the coating from peeling off the hook mesh, hook tennis court chain link fence systems have long tended to define lines that economically attach amenities and add value to the property. The interlocking system also allows deductions for easy attachment control.

The cooling circulation system uses spray to cool the drawing die, and takes away a lot of heat generated by the drawing machine in high speed drawing in time to ensure the quality of the wire. Control drawing process parameters: drawing speed 10 ~ 12m/s; Winding tension 8 ~ 10N; Measuring length 30km; The mass fraction of lubricant is 3.5 ~ 4.5%; pH value of lubricant 7 ~ 8; Lubricant temperature 30 ~ 40℃.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.