The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate. The concentration of plating aid should not be too high. Hot plating wire must be added ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution is controlled in the range of 50~80g/L. The addition of ammonium chloride or zinc chloride raw materials without the results of laboratory analysis shall be subject to criticism and education, and economic treatment if necessary.

6, according to the wire diameter thickness to adjust zinc dipping time. Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is the length of the distance between the lead screw on the zinc pot and the ceramic sinking roll. The zinc dipping time of coarse wire diameter should be long, and the zinc dipping time of fine wire diameter should be short.

In strict accordance with the multi-pass small compression rate drawing, the total compression rate is 96.48%, reducing the scraping of zinc layer. The whole wire drawing die is made of tungsten steel die and polycrystalline die. The Angle of the working cone of the wire drawing die is 12° ~ 16°, and the length of the sizing belt is 0.15 of the diameter of the wire, so as to ensure that the deformation of the zinc layer is basically synchronous with the steel wire substrate.

Zinc pot workers should be determined to do duty and responsibility. Do not leave the post without leave, always observe the change of hot plating wire galvanized layer, and according to the analysis results, master the asbestos block gap friction, how long it takes to press, replace the pressing face; Adjust the working face; Until all four faces of the asbestos block are used up, maintenance workers can continue to use the asbestos block after repair when necessary to reduce the consumption of asbestos block.

If the zinc coating is good, but in 3% nitric acid when the light, the coating has dark shadow, passivation occurs when the film is brown, may be caused by foreign metal impurities such as copper or lead in the galvanizing liquid. When problems occur in the process of galvanizing large coil galvanized wire, the temperature and current density are checked first, and then the content of zinc and sodium hydroxide in the plating solution is measured and adjusted through the analysis of the plating solution. Whether DPE content is low can be determined by hull cell test.

Annealing wire is widely used mainly because it has a good elasticity and flexibility, in the annealing process can be a good control of its hardness and softness, it is mainly made of iron wire, more commonly used in the construction industry tie wire use. When the wire factory is in production, the annealing wire will be processed according to the performance of the material, and its hardness will be changed according to the different demand, which can make it have more advantages, reduce the consumption of metal and reduce the cost of production.

Now more and more people are buying the barbed rope, but there are often a lot of people do not know the specifications of the blade barbed rope when they buy, here is to introduce the specific characteristics of the blade barbed rope.