Compared with galvanizing, hot-dip galvanizing has lower production cost and less environmental impact than galvanizing. Because the coating obtained is thicker, hot-dip galvanizing has better protective performance than electric galvanizing, so it is an important protective coating for steel parts used in harsh working environment. Hot-dip galvanized products are widely used in chemical equipment, petroleum processing, ocean exploration, metal structure, electric power transmission, shipbuilding and other industries.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

Good galvanized wire, plating thickness of 3- 4 mm, zinc adhesion should be less than 460 grams/m, that is, the average thickness of zinc layer is not less than 65 microns. When the thickness of plated parts is greater than 4 mm, the zinc adhesion should not be less than 610 g/m, that is, the average thickness of zinc layer should not be less than 86 microns. Standard galvanized wire coating must be uniform, galvanized layer basically uniform with copper sulfate solution test etching five times no dew iron. For standard galvanized wire coating adhesion requirements, the zinc layer of plated parts should be firmly combined with the basic metal and have enough adhesion strength, after hammer test does not fall off, not convex.

Welding electrode has a wide range of applications, can realize a variety of materials, a variety of profiles and a variety of joint forms of welding.

1. Adjust electroplating process parameters

Generally, the main reasons for the rust of iron wire are: when the steel mesh in the metal mesh appears some dust, this time you can use some water or alkaline solution cleaning. Followed by floating iron or embedded iron, iron will rust, connected to the stainless steel plate mesh of iron rust, so these iron must be dealt with, can use carbon steel wire brush can also be used for processing carbon steel and so on. Then is the scratch, for the scratch, mainly in the production process, need some stubborn iron scratch stainless steel plate net special polishing cleaning machine.

4,  galvanized can be used zincate galvanized or chloride galvanized process, should use appropriate additives to meet the requirements of this standard coating.

The application of electric welding net is more widely, at present it has replaced the use of other parts of the wire mesh, the cost of electric welding net is lower, the production speed is very fast, so it is very popular. Welding net galvanized before the need for processing is recrystallization annealing, because the welding net must maintain a no oxide and no other impurities of pure iron active surface, if you can not keep its surface clean will lead to a bad galvanizing effect, galvanized layer and iron material is not closely combined, so this step is necessary.