The diameter of cold-drawn wire should conform to the contract, check whether the amount of zinc meets the requirements of the contract, check the tensile strength, and ask the factory to provide the corresponding inspection report. The wire factory introduces that the weight of a single coil of wire of different specifications should not be lower than the volume weight required by the contract, and record the value. No contacts are generated for each reel of wire. If there are contacts, no more than three contacts are generated for each reel. Each contact should be smooth surface treatment, the wire can not be pulled off from the contact, in line with customer packaging requirements.

2. Use a large pickpocket to stir the zinc ash before the steel wire enters the zinc liquid; Use a small outlet for the galvanized steel wire; Zinc pot steel wire outlet in 30 minutes, with pickpockets back and forth, until the large, floating zinc residue into brown, real zinc ash, zinc ash surface. After the removal of zinc ash should be brown yellow real zinc ash, zinc surface, effectively reduce zinc consumption. This is one of the measures to reduce zinc consumption, but it is also a real problem, which has not been solved for many years.

6, passivation to remove hydrogen parts should be passivation after the removal of hydrogen, passivation before the application of 1%H2SO4 or 1% hydrochloric acid activation 5~15s. Passivation shall be treated with colored chromate unless otherwise specified in the design drawings.

Wire mesh welding after galvanized is through the end of the welding and then the cold company to make wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot galvanized. After the first galvanized welding is to change the wire mesh, after the end of welding can see the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the appearance is smooth, and the cost of the first welding after plating is higher, not easy to rust.

The difference is that hot dip galvanizing is dipped in zinc solution melted by heating, which has fast production speed and thick but uneven coating. The color is dark, the consumption of zinc metal is much, the formation of infiltration layer with the matrix metal, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can be maintained for decades. Cold galvanized is in the plating tank through the current unidirectional zinc gradually plated on the metal surface, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust.

Steel mesh galvanized: galvanized refers to the surface of metal, alloy or other materials coated with a layer of zinc to play a beautiful, rust prevention and other surface disposal technology. Now the first choice of method is hot dip galvanized, galvanized solution has cyanide bath and cyanide-free bath two categories. Cyanide bath bisects micro cyanide, low cyanide, medium cyanide, and high cyanide.

Stainless steel barbed rope in the way of corrosion is not very, because the surface is not treated but rely on its own raw materials for corrosion resistance, so there will be no chemical reaction. After a long time of use, it will not rust like the corrosion layer on the surface of hot dip galvanized barbed rope, because the internal material of stainless steel barbed rope is the same as the material on the surface. The most obvious difference in a short time is the cross section of this piece, hot dip galvanized barbed wire because of surface anticorrosion treatment, so there will be rust in the cross section of this piece, and stainless steel barbed wire because the internal raw materials and surface raw materials are consistent, so there is no such situation.