After the optimization of the process, mass production of 0.80mm electro galvanized steel wire electro galvanized zinc layer quality is controlled within 80 ~ 90g/m2, zinc layer quality dispersion is very small; The results show that the average weight of zinc layer is 14.5g/m2, the loss of zinc layer is less than 5%, and the tensile strength of steel wire is 2300 ~ 2500MPa. It not only effectively controls the quality of zinc layer of raw steel wire, but also reduces unnecessary waste and production cost.

Some large roll galvanized wire products in order to meet different industrial needs, will be further processed on the surface, such as the anti-corrosion layer, galvanized, iron plating, aluminum alloy plating, or in the galvanized wire appearance above the copper plating, brass plating, etc., to strengthen the steel wire and colloidal years and capabilities. Generally, galvanized wire products should be well plated and drawn when they are produced, and the sequence of the two processes should be decided according to the production or industrial needs.

Low and medium carbon steel wire is used as raw material, with good surface gloss, uniform zinc layer, strong adhesion, corrosion resistance and so on. Available: diameter 1.60mm-4mm (16#-33#) cold plating wire; Diameter 6.40mm-0.81mm(8#-21#) black iron wire, changed wire. It is mainly used in communication equipment, medical equipment, weaving net, brush, steel cable, filter, high-pressure pipe, construction, crafts and other industries.

Galvanized hook mesh standard is thorough, mesh planning: 3cm-20cm, silk planning: 1.2mm-4.5mm, galvanized hook mesh 6000 square meters, some standards are available. Benefits: The selection of low carbon steel wire, surface for cold galvanized (electric galvanized) hot dip galvanized anticorrosion treatment, mesh wire strong, strong protection, long anticorrosion time.

Electric galvanized wire direct selling is in the plating tank through the current one-way to gradually zinc plating on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, poor corrosion resistance, generally a few months will rust. Compared with hot dip galvanizing, the production cost of electric galvanizing is lower. The difference between cold galvanizing and hot galvanizing: the difference between cold galvanizing and hot galvanizing is that the amount of zinc is different. They can be identified from the color. The color of cold galvanizing is shiny silver white with yellow. Hot dip galvanizing shiny white.