Hexagonal mesh is also known as twisting mesh, thermal insulation net, soft edge net. Material: low carbon steel wire, stainless steel wire, PVC wire, copper wire knitting: straight twist, reverse twist, two-way twist, first after plating, first plating after knitting, and hot dip galvanized, zinc aluminum alloy, galvanizing, PVC coated, etc. Features: Solid structure, flat surface, with good corrosion resistance, oxidation resistance and other characteristics. Uses: Used for raising chickens, ducks, geese, rabbits and zoo fences, mechanical equipment protection, highway guardrail, etc.

Large roll galvanized wire phosphating film is dark gray to black gray, the thickness is generally 5-20μm, has better corrosion resistance in the atmosphere. Membrane is a microporous structure, strong adsorption ability to paint, such as used as paint bottom, corrosion resistance can be further advanced. Metal oxidation treatment: Add steel products to NaOH and NaNO2 mixed solution, heating treatment, the surface can form a layer of thickness of about 0.5-1.5μm blue oxide film, in order to reach the purpose of steel corrosion prevention, this process is called blue treatment, referred to as blue.

Heavy duty hexagonal mesh made of steel wire by special machinery woven into a hexagonal mesh net. This kind of mesh can be cut and assembled into fence mesh, mountain hanging mesh, vegetation three-dimensional mesh, composite, etc. Aliases: Gabion mesh, heavy hexagonal mesh, ecological mesh, wire mesh, etc.

Galvanized iron wire is selected from excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process:

3, hexagonal network customized weight, the greater the weight, the more sufficient the material.

Hot dip galvanizing is to make the molten metal react with the iron matrix to produce an alloy layer, so that the matrix and the coating are combined. Hot dip galvanizing is to first pickling the iron and steel parts. In order to remove the iron oxide on the surface of the iron and steel parts, after pickling, it is cleaned in the tank of ammonium chloride or zinc chloride aqueous solution or mixed aqueous solution of ammonium chloride and zinc chloride, and then sent into the hot dip plating tank. Hot dip galvanizing has the advantages of uniform coating, strong adhesion and long service life.

Hardness is a commonly used property index in mechanical properties of metal materials. The iron wire factory introduces a fast and economical test method for hardness testing. However, for the hardness of metal materials, there is not a unified and clear definition including all test methods at home and abroad. In general, the hardness of a metal is often considered to be the resistance of the material to plastic deformation, scratches, wear, or cutting.