In the calculation process of 12*14 specifications of barbed rope, it can not be calculated according to the above calculation formula, because first of all, two specifications of raw materials are used, the thinner the wire diameter, the higher the processing cost. Generally speaking, a kilogram of 12*14 barbed rope can reach about 7.5 meters, and the ratio of warp wire to barbed rope cannot be calculated according to the traditional ratio of 7 to 3. The specific use of how much wire and silk need to go through a series of professional measurement but also increase the loss of raw materials and other factors to calculate. Thorn rope factory will also according to customer needs to calculate the reasonable amount of customer use.

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

Thorn rope factory production per ton of product profit is not particularly high so in the sales price to wholesale, many users always think that thorn rope price has a lot of profit space so they are eager to lower the price, some manufacturers in order to sell out on the use of low price promise and then underweight behavior. Often the actual user spends less money with the lack of weight is almost the same, so the unit price is relatively high. Because the quotations of the thorn rope factory are in accordance with the real price, the quality is guaranteed. In this way, the customers will not look for debts after the purchase, and the subsequent purchase work will still find us, so that we can benefit.

Large roll galvanized wire is made of low carbon steel wire rod processing, is made of low carbon steel, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other surface treatment process processing. Large roll galvanized wire is divided into hot dip galvanized wire and cold galvanized wire (electric galvanized wire). Although galvanized galvanized wire and silver powder paint spray effect appearance is not much different. But the effect is very different, galvanized wire surface is zinc layer, good adhesion, good corrosion resistance.

We compare the difference between galvanized welding net and other welding net by introducing in detail, and write the following to introduce its material: Galvanized welded wire mesh is made of low carbon wire, through automation of fine precision machinery equipment spot welding processing after forming, selection of disposal of the appearance of zinc leaching technology, produce practice British standard, with smooth surface neat, uniform layout to consolidate, the function is good, even if some sections or accept pressure also won’t attack lax appearances, it is the strongest anti-corrosion function in iron mesh, Screen mesh is iron use one of the most widely network class, excellent anticorrosive makes its popularity in the breeding, sucking the neat surface, increased the look and feel, can play will be decorating effect, this feature makes it reflected in the mining industry, because the select material of low carbon high quality material, make it unique iron mesh not usually have flexibility, Concluded that it is used in the process of plasticity, and then can be used for the deep processing of hardware technology, disorderly wall swing, underground leak-proof crack, light net body, make this cost is much lower than the cost of iron screen, more can understand its economy, benefits. Galvanized welding net can be used as poultry cage, egg basket, channel fence, drainage tank, porch fence, rat net, mechanical protective cover, livestock and plant fence, grid frame, etc. It is also widely used in industry, agriculture, construction, transportation, mining and other occupations.

Therefore, when zinc reaches saturation in the solid melt, the two elements of zinc and iron atoms diffuse with each other, and the zinc atoms diffused into (or infiltrated into) the iron matrix migrate in the lattice of the matrix and gradually form an alloy with iron, while the iron diffused into the molten zinc liquid forms an intermetallic compound FeZn13 with zinc and sinks into the bottom of the hot-dip galvanized pot, that is, zinc slag. When the workpiece is removed from the zinc leaching solution, the surface of the pure zinc layer is formed, which is hexagonal crystal, and its iron content is not more than 0.003%.

Zinc is a silver-white metal, brittle at room temperature, soluble in acid and alkali, known as amphoteric metal. Pure zinc is more stable in dry air, and small in humid air or water containing carbon dioxide and oxygen. A thin film layer of basic zinc carbonate will be formed on the surface, which can delay the corrosion rate of zinc layer. The corrosion resistance of galvanized layer in aqueous solution of acid, alkali and sodium chloride is relatively strong. It is also not resistant to corrosion in atmospheres containing carbon dioxide and hydrogen sulfide and in Marine atmospheres; In high temperature and high humidity air and containing organic acid atmosphere is small, galvanized layer is also easy to be corroded.