Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.

Every galvanized wire production into the peak season of the industry, the road to the factory will from time to time see transportation wire and container container vehicles, as well as galvanized bright silk short-distance transportation trucks, led to the utilization of labor in the surrounding countryside, solved the employment problem of most people. Galvanized wire is divided into hot plating wire and cold plating wire.

The price of galvanized iron wire is relatively low, but the corrosion resistance is excellent, so it is favored by many screen businesses. In the production process of galvanized iron wire, first of all, we should check the equipment to see if there are any problems, and then we should look at the galvanized process, whether there are factors that cause product discoloration. If these problems do not exist, or some of them occur on the same equipment, and some are normal, then we should consider the problem of raw materials at this time.

The main difference is carbon content. Iron has a carbon content of 2.11 percent or more, while steel has a carbon content of 2.11 percent or less. Iron-carbon alloys with carbon content of more than 2.11% are cast iron (pig iron), which are basically not malleable and cannot be drawn into wire. Secondly, the content of impurities is different, and the content of harmful impurities such as sulfur and phosphorus in steel is smaller. Wire general color key, wire color light point, white point.

There are many categories of large rolls of galvanized wire, and different categories can be applied to different scenarios. The common application of galvanized iron wire is the application of the construction industry. One is the use of binding wire. Whether it is the binding of scaffolding or reinforcement, galvanized iron wire is needed to carry out. There are also 20kg or 50kg bundles of No. 18, No. 16, No. 14, No. 12, No. 10 galvanized coils.

Cold wire drawing is a kind of cold processing of metal. The raw material is wire rod, which is produced by peeling, galvanizing and other processes. Galvanized cold drawing is used more in building materials. Its testing standards are also different. The strength of cold drawing is relatively high. Because of the high strength of steel, it plays a very important role in construction. It saves the construction steel in building materials, and also reduces the cost of the project. It also plays a very important role in the structure of concrete.

The management system of the rinsing water after the steel wire pickling should be regularly and regularly discharged after the rinsing water, and the rinsing water should be kept clean and low acid value as far as possible. The pH control is more appropriate. The concentration of plating aid should not be too high. Hot plating wire must be added ammonium chloride and zinc chloride according to the data of laboratory analysis, and the specific gravity of the composite solution is controlled in the range of 50~80g/L. The addition of ammonium chloride or zinc chloride raw materials without the results of laboratory analysis shall be subject to criticism and education, and economic treatment if necessary.

Cold galvanized, generally speaking, do not need heating, galvanized amount is little, this galvanized parts are easy to fall off in wet environment. Hot dip galvanizing, also known as hot dip galvanizing, is to melt the zinc ingot at high temperature, put some auxiliary materials in, and then dip the metal structural parts into the galvanized groove, so that the metal members are attached to a layer of zinc layer. The advantage of hot dip galvanized is that its anticorrosion ability is strong, the adhesion and hardness of galvanized layer is better.

Excellent anticorrosive makes its popularity in the feed, the net surface smooth and tidy, increased the look and feel, can be adornment effect, this characteristic makes it to show in the mining industry, due to high quality with low carbon materials as raw materials, to make it unique general iron mesh screen does not have flexibility, determine its plasticity in use process, Thus can be used in the hardware process of deep processing and manufacturing, complex wall batch swing, underground leakage prevention cracking, light mesh body, so that the cost is much lower than the cost of iron screen, more able to understand its economic and practical.