In the process of production, the acid activation solution can remove the corrosion products and oxide film on the surface of low carbon steel wire without excessive corrosion on the matrix. Galvanized wire can be used zincate galvanized or chloride galvanized process, appropriate additives should be used to obtain the coating required by the standards of low carbon steel wire. When galvanized wire out of the light plating should be carried out light treatment. The bath temperature of galvanized wire should be controlled well.

Galvanized iron wire will rust, mainly and the thickness of galvanized layer and the use of the environment, galvanized iron wire is also divided into cold galvanized iron wire and hot galvanized iron wire, in general, hot galvanized iron wire galvanized layer is thicker, rust prevention time is longer, generally can be 7 or 8 years without rust. If the galvanized layer is damaged, or long-term use in a humid environment, it will accelerate the rust time of galvanized iron wire.

Stainless steel material refers to air, steam, water and other weak corrosive medium and acid, alkali, salt and other chemical corrosion medium corrosion of steel, also known as stainless acid steel. In practical application, the steel with weak corrosion resistance is often called stainless steel, and the steel with chemical corrosion resistance is called acid resistant steel. And galvanized wire has good toughness and elasticity, zinc can reach 300 grams/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance. Products are widely used in construction, handicrafts, silk screen preparation, highway guardrail, product packaging and daily civil and other fields.

After proper heat treatment or cold drawing hardening, high carbon steel wire has high strength and hardness, high elastic limit and fatigue limit (especially notched fatigue limit), cutting function is acceptable, but welding function and cold plastic deformation ability is poor.

For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by customers. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this thing is more important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized silk, the weight can reach 300kg/ roll or 800kg/ roll.

Annealed wire is a soft iron wire made of low carbon steel cold drawing, heating, constant temperature, heat preservation and other processes. The composition of iron wire varies according to its use. It contains iron, cobalt, nickel, copper, carbon, zinc, and other elements. The hot metal billet rolled into 6.5mm thick steel bar is the wire rod, and then put it into the wire drawing device into a different diameter of the line, and gradually reduce the aperture of the wire tray, cooling, annealing, plating and other processing technology made of various specifications of iron wire.

Wire mesh welding after galvanized is through the end of the welding and then the cold company to make wire mesh wire mesh steel mesh construction mesh floor heating mesh galvanized or hot galvanized. After the first galvanized welding is to change the wire mesh, after the end of welding can see the welding spot; The two processes are different prices are also very different, the cost of the first plating after welding is low, the appearance is smooth, and the cost of the first welding after plating is higher, not easy to rust.