Galvanized wire coating rough, passivation film is not bright, bath temperature is too high. If the cathode current density is too high, zinc content in the bath is too high or sodium hydroxide and DPE content is too low; Electroplating solution with solid particles or excessive foreign metal impurities, will lead to such problems. Solution: If the large roll galvanized wire to the above coating is rough, there may be solid particles in the plating solution. If the roughness of the part is severe, the current density may be too high.

The bonding and anchoring function between cold wire drawing and cold rolled ribbed steel bar and concrete is outstanding. Therefore, when used in components, the phenomenon of cracking of component anchorage area and damage caused by steel wire slip is fundamentally eliminated, and the load-bearing ability and anti-cracking ability of component end are improved. In reinforced concrete structure, the crack width is smaller than that of circular steel bar or even that of hot rolled thread bar.

The barbed rope factory not only provides the sales work of blade barbed rope, including the subsequent construction, but also contracted together, and the construction price is particularly different.

The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the surface will gradually lose its role because of the oxidation reaction, which is more prominent in the humid environment. And because the use of rusty wire after all, it is said that the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

The thorn rope belongs to the weaving industry, so it is less affected by environmental protection. The thorn rope will not be discarded in the production process, and it belongs to the weaving industry, so the situation is less affected by environmental protection.

Electrode application range is wide, can realize a variety of materials, a variety of profiles and a variety of joint forms of welding. (1) Welding between low carbon steel, low alloy steel, medium carbon steel, alloy steel and other metal materials or dissimilar metal materials can be achieved. The weld has good comprehensive mechanical properties, and the tensile strength can reach more than 400MPa. ⑵ Can realize the welding of large plate, steel frame, plate – tube, rod – rod, tube – tube and other profiles. ⑶, can realize docking, Angle, lap, T joint and other joint forms of welding. ⑷ mainly suitable for flat welding.(5) it can surfacing the parts of wear failure, so as to obtain the surface surfacing layer with melting depth, smooth surface and excellent performance. ⑹ It can be realized that no bevel 1 ~ 6mm thick metal sheet single-side welding double-side molding.

The formation process of hot dip galvanized layer is the process of forming iron-zinc alloy between the iron matrix and the outside pure zinc layer. The surface of the workpiece forms the iron-zinc alloy layer during the hot dip plating, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc solution, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the gravitational attraction between the atoms is relatively small.

Field fence line net is a streamlined, streamlined, beautiful, tacky, fashionable European elegance; The diversity of color selection, a variety of standard color card colors to choose from, can meet different varieties, different, different needs. On-site fence line can be separated from a variety of methods, and according to the customer’s disagreement request.