Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.

Generally, the main reasons for the rust of iron wire are: when the steel mesh in the metal mesh appears some dust, this time you can use some water or alkaline solution cleaning. Followed by floating iron or embedded iron, iron will rust, connected to the stainless steel plate mesh of iron rust, so these iron must be dealt with, can use carbon steel wire brush can also be used for processing carbon steel and so on. Then is the scratch, for the scratch, mainly in the production process, need some stubborn iron scratch stainless steel plate net special polishing cleaning machine.

According to the galvanized iron wire manufacturer, galvanized iron wire is the selection of excellent low carbon steel, through drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized, cooling and other processes. Galvanized iron wire should pay attention to the following points in the use process:

Its wire diameter specifications include: 8#-24#, with thick coating, corrosion resistance, strong coating and so on. And according to the special needs of users, according to industry standards to provide various specifications of galvanized wire. Low carbon steel wire is called galvanized iron wire after drawing and galvanized, so galvanized wire products have certain characteristics. In order to better let galvanized wire play an effect, in the process of galvanized wire, generally according to customer needs to control the thickness of galvanized wire zinc layer, so that galvanized wire can meet the needs of customers.

1. Principle. Because zinc does not change easily in dry air, and in humid air, the surface can form a very dense film of zinc carbonate, which can effectively protect the interior from corrosion. And when the coating is damaged for some reason and the matrix is not too large, the zinc and steel matrix form a micro cell, so that the fastener matrix becomes the cathode and is protected. It is widely used in automobile transportation and other industries, but what is needed is the trivalent chromium passivation layer, zinc nickel alloy plating closed coating, reduce the harmful and toxic layer of hexavalent chromium passivation.

The price of galvanized iron wire performance is the key to win, galvanized wire only with good performance, in order to win the market, in order to obtain customer praise. In galvanized wire, the main function of carbon in increasing hardness, less is less easy to rust, the main function of chromium is acid and alkali resistance; Nickel’s main function is high temperature resistance, acid and alkali resistance and conductive use; The main function of iron is magnetic conductivity; The main functions of titanium are low density, high hardness and strong corrosion resistance. The main function of copper is magnetic and electrical conductivity. Different chemical components have different functions, which together form the characteristics of galvanized wire.

Many people do not know how to choose high quality cut wire, I will give you a detailed introduction. The raw material of cutting wire is divided into: stainless steel cutting wire, copper cutting wire, steel wire cutting wire, copper plated steel wire cutting wire, galvanized steel wire cutting wire, iron wire cutting wire, aluminum wire cutting wire and so on.

Galvanized barbed wire as a safety protection of the metal wall, the galvanized barbed wire device also need to be protected for a long time? And how to protect it? Maintenance and protection of galvanized barbed rope. First, we can start from two aspects. One is about the protection of galvanized barbed rope posts.

The different spacing of the thorn rope is mainly in order to save costs to consider, because if they are too close, then obviously a little waste of resources, but the installation is too sparse will not work. Usually the bottom spacing is about 10cm, and the top is up to 20cm, this is because the higher the place is more difficult to climb over, usually more than one meter without the help of tools it is difficult for ordinary people to climb over, and the bottom because of the relatively tight can prevent personnel from drilling in the past.

Large rolls of galvanized silk play a very important role in our life. Made of low carbon steel rod processing, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other process processes. Galvanized wire is divided into hot galvanized wire and cold galvanized wire (electric galvanized wire). Galvanized iron wire has good toughness and elasticity, the amount of zinc can reach 300 g/square meter. It has the characteristics of thick galvanized layer and strong corrosion resistance.

Hot dip galvanizing is also called hot dip zinc and hot dip galvanizing: is an effective way of metal corrosion, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel parts is attached with zinc layer, so as to play the purpose of anticorrosion. Hot dip galvanizing process: finished product pickling – washing – adding bath aid – drying – hanging plating – cooling – drug – cleaning – grinding – hot dip galvanizing completion. Hot dip galvanizing is developed from the older method of hot dip galvanizing. It has a history of 140 years since it was applied to industry in France in 1836. However, the hot dip galvanizing industry has been developed on a large scale in the past 30 years with the rapid development of hot dip galvanizing wire.