The service condition and service life of electro galvanized iron wire or component are closely related to the thickness of electroplated coating. The more strict the conditions of use and the longer the service life, the thicker the layer of galvanized iron wire required. Different products, according to the specific environment (temperature, humidity, rainfall, atmospheric composition, etc.) to determine the expected service life of the coating thickness, blind thickening will cause all kinds of waste. But if the thickness is insufficient, it will not reach the expected service life requirements. Different manufacturers, according to their own equipment conditions, in the case of determining the plating, the first preparation of a more complete and reasonable process flow, clear plating parameters, control plating solution concentration, standard operation.
Post time: 02-03-23
Different from the general zinc barbed rope, the zinc content of the surface of the high zinc barbed rope is very high, which can reach 6-8 times of the former, so that it has a great advantage in service life. Ordinary products begin to corrosion in three or five years, while the latter takes longer time to change. Stainless steel barbed rope is in the material aspect of protection so durability is also better, these two products are known for long service life, but is high in price.
Large roll galvanized wire is made of low carbon steel wire rod processing, is made of low carbon steel, after drawing forming, pickling rust removal, high temperature annealing, hot dip galvanized. Cooling and other surface treatment process processing. Large roll galvanized wire is divided into hot dip galvanized wire and cold galvanized wire (electric galvanized wire). Although galvanized galvanized wire and silver powder paint spray effect appearance is not much different. But the effect is very different, galvanized wire surface is zinc layer, good adhesion, good corrosion resistance.
Two, cold galvanized wire production process of galvanized. Galvanizing is the core process in the production of cold galvanized wire, mainly by soaking the steel wire in a molten zinc solution to form a zinc layer on its surface.
Its specific design layout principle is:
Post time: 19-08-22
There are many kinds of zinc plating solution, which can be divided into plating solution and no plating solution according to its properties. The galvanized liquid has good dispersion and covering property, the coating crystal is smooth and fine, the operation is simple, the application range is wide, and the long-term use is in the production. However, due to the toxic substances contained in the plating solution, the gas escaping from the plating process has great harm to the health of workers, and the waste water must be treated strictly before discharge.
The second is price.
Post time: 06-05-23
Because of the large size of the barbed rope, the rope factory is used to packing. If you do not pack, then a load of blade rope can not hold many pieces, but also relatively occupy space and easy to be lost in the process of transportation.
Galvanized iron wire is very common in practical application, some people think that galvanized iron wire will not rust, in fact, it is not. Metal corrosion is caused by the chemical or electrochemical action of the surrounding medium. According to different media, it is divided into atmospheric corrosion, soil corrosion, seawater corrosion, bacterial corrosion and so on. Atmospheric corrosion is more common, because metal products in the process of processing, transportation and storage, when in contact with the atmosphere, there are always atmospheric corrosion conditions.
Post time: 09-06-22
Steel mesh benefits: Compared with traditional handmade steel mesh, steel mesh has better elasticity and even spacing. When pouring concrete, the steel mesh is not easy to bend, and the thickness of concrete protective layer is easy to control and even. In bridge deck surfacing, measure the protective layer of steel mesh. The pass rate is 95 percent.
The basic requirements are the flatness of the net surface, hook mesh first after weaving, weaving process, rolling flowers can not turn, to adhere to smooth, can not present wire or turn flowers.
On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.
Post time: 28-06-22
1. Grid structure is simple, beautiful and practical; 2. Easy to transport, installation is not limited by terrain relief; 3. Especially for mountain, slope, multi-curved area adaptability; 4. Medium low price, suitable for large area use. Main market: railway, highway closed net, yard fence, residential guardrail, all kinds of isolation net.
PVC coated barbed rope is widely used for railway highway protection, but also for safety protection of rivers, embankments and seawalls, so as to better protect the safety of people and animals.
Post time: 07-07-22
When the zinc layer is seriously damaged and endangers the iron matrix, the zinc will produce electrochemical protection on the matrix, the standard potential of zinc is -0.76V and the standard potential of iron is -0.44V. When zinc and iron form microbatteries, the zinc will be dissolved as the anode, and the iron will be protected as the cathode. Obviously, the atmospheric corrosion resistance of hot dip galvanizing is better than that of electric galvanizing.
However, in the actual production process, the wire may be affected by other factors that may cause the wire to lose its conductive properties. For example, if the thickness of the galvanized layer is too thick or the surface is not uniform, the current density on the surface of the wire will be uneven, which will reduce the electrical conductivity of the wire. Similarly, if the wire is stretched too much during wire drawing, it may cause the wire to break or the surface to deform, thus affecting its electrical conductivity.