Decorative hook mesh selection of stainless steel, aluminum alloy, brass, copper and other alloy materials, through the special process of preparation of hook mesh. It is a silk screen made of decoration. Today we introduce the aperture and wire diameter of the decorative hook mesh.

Paint on the galvanized layer, the binding force between each other and the baking temperature of the paint has a great relationship, after galvanized coating alkyd paint, adhesion is no problem. Galvanized amino paint, paint adhesion is not good. Do two bottom two surface, adhesion is ok, if the two bottom two surface to two bottom three surface, that is, more paint, more baking once, again test adhesion is very poor, poor to the paint from the galvanized layer of pieces torn off.

When buying large galvanized wire, first look at the hardness of galvanized wire, only after the hardness reaches the standard can be used. The hardness standard of large coil galvanized wire is a very important performance index and an economical test method. However, for the hardness of metal materials, there is not a unified and clear definition including all test methods at home and abroad.

The barbed rope factory will store the blade barbed rope in a suitable place when it is stored, because it understands the product characteristics.

Although galvanized iron wire has the protection of galvanized layer, it does not say that it will not rust at all, but delays the time of rust. In general, cold galvanized iron wire can be kept for 1-2 years without rust, hot galvanized iron wire can be used for 8-10 years without rust. If properly maintained, the use time will be longer. So how to prevent galvanized iron wire rust?

Paint on the galvanized layer, the bonding force between each other has a great relationship with the baking temperature of the paint, and alkyd paint is coated after galvanized, and the adhesion is not a problem. After galvanized to do amino paint, paint adhesion is not very good. Do two bottom two surface, adhesion is good, if the two bottom two surface changed to two bottom three surface, that is, more paint, more baked once, again test adhesion is very bad, bad enough to tear the paint from the galvanized layer.

Some customers pay more attention to the quality problem, so they pay more attention to the service life. The barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.

On the contrary, the denser the ion deposition, the better the quality of zinc layer. Under the condition that the surface zinc layer is dense and bright, the quality of zinc layer per unit area should reach 80g/m2, and the process parameters should be optimized as follows: current density is 16-20A /dm2, mass concentration of zinc sulfate solution is 500g/L, and pH value is 2.5-3.0.

Hot dip galvanizing is also called hot dip zinc and hot dip galvanizing: is an effective way of metal corrosion, mainly used in various industries of metal structure facilities. It is to immerse the steel parts after rust removal into the molten zinc liquid at about 500℃, so that the surface of the steel parts is attached with zinc layer, so as to play the purpose of anticorrosion. Hot dip galvanizing process: finished product pickling – washing – adding bath aid – drying – hanging plating – cooling – drug – cleaning – grinding – hot dip galvanizing completion. Hot dip galvanizing is developed from the older method of hot dip galvanizing. It has a history of 140 years since it was applied to industry in France in 1836. However, the hot dip galvanizing industry has been developed on a large scale in the past 30 years with the rapid development of hot dip galvanizing wire.

When the zinc layer is seriously damaged and endangers the iron matrix, the zinc will produce electrochemical protection on the matrix, the standard potential of zinc is -0.76V and the standard potential of iron is -0.44V. When zinc and iron form microbatteries, the zinc will be dissolved as the anode, and the iron will be protected as the cathode. Obviously, the atmospheric corrosion resistance of hot dip galvanizing is better than that of electric galvanizing.

Welding net is widely used in industry, agriculture, breeding, construction, transportation, mining and other aspects. Such as machine shields, animal pens, flower pens, window bars, access fences, poultry cages, egg baskets and home office food baskets, paper baskets and decorative items.