Benefits of Using Tek Screws
Understanding Wafer Head Tek Screws
Operating procedures: When using cold galvanized wire, all tools and stacked objects obstructing activities should be removed from the work site and equipment. When pickling, put the wire into the cylinder slowly to prevent acid splashing on the body. When adding acid, it is necessary to pour the acid into the water slowly. It is forbidden to pour the water into the acid to prevent the acid from splashing out. Wear protective glasses when working. Do not push or beat cold galvanized wire and other articles when handling them.
Pet cage has many types, and selective is bigger, pet cages are generally made of wire, with better coarse, then at the bottom with a wheel base, such a simple pet basket was made, in the wheel at the bottom of the mount is for the convenience of the mobile, a pet cages should also adapt to the location of the production in addition to a door, It is convenient for feeding pets.
The material of small hexagonal net is the same as that of other hexagonal net, which is generally made of low carbon steel wire, stainless steel wire and galvanized steel wire as raw materials by the hexagonal net machine.
Some customers are more concerned about quality problems, so for the service life is more important, barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.
Barbed wire production of general selection of low carbon iron wire, after fine and accurate active welding equipment processing, the selection of galvanized process surface treatment. After the completion of the product, the net surface is smooth and regular, good integrity, strong consolidation, even if part of the trade-off or under pressure will not appear lax phenomenon.
Strictly control the pH value of large roll galvanized wire bath, research shows that the size of the bath pH value directly affects the quality of steel wire coating, improper control of pH value will cause loose coating. When the pH value is greater than 3, the steel wire coating has burr caused by fine dendrites, and the surface is not smooth. The current density is strictly controlled. From the microscopic morphology, the higher the current density, the larger the zinc layer grain deposition, the less dense the corresponding zinc layer.
If the zinc coating is good, but when the light comes out in 3% nitric acid, there is a dark shadow on the coating, and the film is brown when passivation occurs, which may be caused by foreign metal impurities such as copper or lead in the galvanized liquid. When there is a problem in the process of galvanizing, check the temperature and current density first, and then measure and adjust the content of zinc and sodium hydroxide in the bath through the analysis of the bath. Whether DPE levels are low can be determined by Hull cell test.
Cold galvanized, generally speaking, do not need heating, galvanized amount is little, this galvanized parts are easy to fall off in wet environment. Hot dip galvanizing, also known as hot dip galvanizing, is to melt the zinc ingot at high temperature, put some auxiliary materials in, and then dip the metal structural parts into the galvanized groove, so that the metal members are attached to a layer of zinc layer. The advantage of hot dip galvanized is that its anticorrosion ability is strong, the adhesion and hardness of galvanized layer is better.
Cold galvanizing is in the plating tank through the current unidirectional zinc gradually plated on the metal appearance, the production speed is slow, uniform coating, thin thickness, usually only 3-15 microns, bright appearance, smooth, high aesthetics, poor corrosion resistance, generally a few months will rust. Hot dip galvanized coating is thicker, generally 30-60 microns, coating corrosion resistance is higher. Suitable for outdoor work of steel parts, such as highway fences, power towers, large size fasteners and other more “rough” workpiece long-term rust prevention.
Some customers are more concerned about quality problems, so for the service life is more important, barbed rope factory will generally recommend the use of high zinc barbed rope or stainless steel barbed rope.
According to the different requirements of the industry, different weights of alloy ingots are put in the smelting furnace according to the standard, such as weaving, Ming, paper, lang, silicon, etc., and the data out of this smelting is called gold ore iron. Iron has gray iron, white iron and the above-mentioned gold, they have different characteristics, so in the industry according to their different characteristics to transport and selection. For example, in gray iron, its carbon exists in iron ore in graphite condition, the crack is often gray, soft and strong, simple filtering, suitable for casting.
The production process of stainless steel blade piercing rope is basically similar to that of galvanized blade piercing rope, and the blade size is usually determined according to the mold.
1. Used for mountain farming, road isolation, large farming enclosure protection, it is recommended that you choose 3mm wire diameter products.