The methods to control the thickness of galvanizing are as follows: you can slow down the lifting speed of the workpiece, control the time of galvanizing as far as possible, add the appropriate amount of thinning alloy, reduce the thickness, and improve the temperature of hot-dip galvanizing. But consider the zinc pot, iron pot should not exceed 480 degrees, ceramic pot can be 530 degrees, which can reduce the time of zinc immersion.

Wire-wall welding net is widely used in industrial production, agriculture, engineering construction, transportation, mining and other processing and manufacturing industries. Such as machinery and equipment protective cover, animal guardrail, pot flower guardrail, window fence, safety exit guardrail, poultry cage, egg basket and home office food industry basket, paper basket and design decoration. It is suitable for general engineering building wall, pouring concrete, multi-storey building, etc., which plays an important structural role in the thermal insulation system. In the construction of the building, the thermal insulation board of hot-dip galvanized electric welding grid is placed on the inside of the outer mold of the wall to be concreted. The external thermal insulation board and the wall are one kind of live, and the thermal insulation board and the wall are integrated into one body after the removal of the mold. The coating on the surface of the weld core is called the coating. The coating of electrode plays a very important role in the welding process. If the photoelectrode without drug skin is used for welding, in the welding process, oxygen and nitrogen in the air will invade a large number of molten metal, metal iron and beneficial elements such as carbon, silicon, manganese oxidation and nitriding to form various oxides and nitrides, and residual in the weld, resulting in slag inclusion or cracks in the weld. The gas in the weld pool may produce a large number of pores in the weld. These factors can greatly reduce the mechanical properties of the weld and make it brittle.

Galvanized iron wire is a substance we often see in life. It is the zinc gradually plated on the metal surface through the unidirectional current in the electroplating tank. The production speed is slow, the coating is uniform, the thickness is thin, usually only 3-15 microns, the appearance is bright, the corrosion resistance is poor, and the corrosion will rust in a few months. Galvanized wire has the characteristics of thick galvanized layer, strong corrosion resistance, strong galvanized layer, etc., the products are widely used in construction, highway walls, Zahua, weaving nets.

For the specification of galvanized wire, the galvanized wire produced by our factory can range from No.8 to No.22, which refers to the BWG standard, that is, from about 4mm to 0.7mm, which can basically cover the type required by the customer. As for the raw material of galvanized wire, normally, we use Q195 mild steel, and some factories will also use SAE1006 or SAE1008. The following is the zinc coating, for galvanized wire, this is very important, the general zinc coating is about 50g/m2 to 80g/m2, some customers need high zinc galvanized wire, zinc coating can reach 200g/m2 to 360g/m2. The tensile strength of galvanized wire is usually 350n/m2 to 800n/m2. Then there is the packaging specification of galvanized wire. The specifications of small rolls of galvanized wire are 50kg/ roll, 100kg/ roll and 200kg/ roll. Of course, there are large rolls of galvanized wire, the weight can reach 300kg/ roll or 800kg/ roll.

Some customers are more concerned about the quality of the problem, so for the service life is more important, thorn rope factory will generally recommend the use of high zinc thorn rope or stainless steel thorn rope.

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

Large rolls of galvanized wire in oxygen violently extinguished, spark, and sodium block, magnesium strip in oxygen extinguished, no spark phenomenon. This phenomenon is determined by the composition of galvanized wire. The galvanized wire used in the experiment is pig iron or steel wire, pig iron and steel are iron and carbon alloy, containing iron and carbon two elements of complex material. Carbon in galvanized wire will produce carbon dioxide when extinguished, solid into gas, volume will shrink rapidly.

The external environment has great influence on the preservation of galvanized wire mesh. In the rainy season, it is necessary to pay attention to the air humidity of the workshop, warehouse and other departments. It is recommended to use a humidifier. Usually, the moisture absorption of book paper is larger than that of powder paper, and the pH value is higher. Generally speaking, in the normal environment of storage wire, storage time of two years is not corroded wire phenomenon. However, it should be noted that in the process of handling the iron wire, it should be handled gently to avoid the position of the coiling coil, which will cause the smooth pulling of the wire and affect the production.