Therefore, the rust of galvanized black iron wire has a great relationship with storage. At the same time, after rust, it is also necessary to conduct reasonable post-processing to avoid affecting its use effect. Of course, when the black iron wire is galvanized, it is also necessary to ensure the thickness of the galvanized layer, so that it can also reduce the possibility of rust. Speaking of galvanized iron wire, perhaps many people think it is relatively rare, in fact, it is not.

Electric galvanized wire is dipped in the zinc solution of heating ablation, the production speed is fast, the coating is thick but not uniform, the market allows a low thickness of 45 microns, up to 300 microns or more. The color is dark, the zinc metal is consumed, and the matrix metal is formed into the entry layer, the corrosion resistance is good, and the outdoor environment of hot dip galvanized can adhere to decades.

With the development of mining industry, pig iron classification in Our country has been very extensive, to meet the needs of the machinery industry. Generally speaking, iron wire factory produces galvanized iron wire iron can be divided into two categories, is directly from the iron ore through iron tracing exercise out of the metal, the primary components of the ore is iron oxide, silica and other miscellaneous stones. When this ore is specially refined into metal iron, the elements such as carbon, silicon, manganese and so on are mixed in, so that the refined data is called – like general pig iron, also for the initial grade of the material.

The weight calculation method of hexagonal net is: the weight calculation method of hexagonal net: silk meridian.× silk meridian.× base x length x width ÷2=kg base: 1/2′=2.151′=1.273/4′=1.65/8′=1.875/4′=1.091′x1/2′ : 3′=0.4 silk warp. x silk warp. X 2x length x width ÷8×3=kg

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

When buying large galvanized wire, first look at the hardness of galvanized wire, only after the hardness reaches the standard can be used. The hardness standard of large coil galvanized wire is a very important performance index and an economical test method. However, for the hardness of metal materials, there is not a unified and clear definition including all test methods at home and abroad.