There are three methods to detect the thickness of zinc layer of galvanized wire: weighing method, cross section microscopy method and magnetic method, among which the first two experiments will cause certain damage to galvanized wire, including the length of galvanized wire and the reduction of dosage. The general detection of galvanized wire galvanized layer is detected by magnetic method, which is also a more intuitive and convenient method. The standard of galvanized layer thickness is related to the wire diameter of galvanized wire. The larger the wire diameter of galvanized wire, the thicker the galvanized layer is. It is the thickness of galvanized layer and cast iron after centrifugal separation.

Customers do not need to worry about the impact of the production cycle when ordering products from the thorn rope factory, because the overall treatment is now focused on the waste gas, so the production of thorn rope should be said to have the least impact. Customers ordering products in the thorn rope factory can rest assured that the delivery time this piece, can provide customers with goods on time. If the production cycle is not affected, then customers will be more assured of the thorn rope factory.

When the coating of large galvanized wire is blistered in the process of galvanizing, the bath temperature should be checked first. If the bath temperature is not low, and then strengthen the removal of oil before plating, to prevent the base metal in acid corrosion. If you pay attention to these problems, the bubbling phenomenon still exists, it should pay attention to the dosage and quality of additives, then you can stop adding additives, with high current electrolysis for a period of time, to reduce the content of additives, observe whether the bubbling phenomenon is improved. If there is no improvement, check whether the additive has been stored for too long or whether it contains too many impurities.

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.

Pet cage is generally made of high quality iron wire, low carbon steel wire, stainless steel wire welding, which is characterized by beautiful, lightweight, folding, easy to store. The surface treatment of pet cage is generally: cold galvanized, hot galvanized, spray, dip, chromium plating, nickel plating and other methods.

The formation process of hot dip galvanized layer is between the iron matrix and the outside of the pure zinc layer, the formation of iron-zinc alloy process, the workpiece surface in hot dip plating when the formation of iron-zinc alloy layer, so that the iron and pure zinc layer is well combined. The process of large roll galvanized wire can be simply described as: when the iron workpiece is immersed in the molten zinc liquid, the first zinc and α-iron (body-centered) solid melt is formed on the interface. This is a crystal formed by the matrix metal iron dissolved with zinc atoms in the solid state. The two metal atoms are fused with each other, and the attraction between the atoms is relatively small.

Paint on the galvanized layer, the bonding force between each other has a great relationship with the baking temperature of the paint, and alkyd paint is coated after galvanized, and the adhesion is not a problem. After galvanized to do amino paint, paint adhesion is not very good. Do two bottom two surface, adhesion is good, if the two bottom two surface changed to two bottom three surface, that is, more paint, more baked once, again test adhesion is very bad, bad enough to tear the paint from the galvanized layer.

The physical methods mainly include manual rust removal and mechanical rust removal, chemical rust removal is generally the use of pickling method, practical application, usually according to the appearance of the workpiece rust status and different post-treatment process, choose different rust removal methods, among which pickling rust cleaning is more commonly used. That is, the iron and steel workpiece with oxide skin or rust is etched in the acid lotion, mainly to remove the oxide or rust layer on the surface of the steel.