Zinc is a silver-white metal, brittle at room temperature, soluble in acid and alkali, known as amphoteric metal. Pure zinc is more stable in dry air, and small in humid air or water containing carbon dioxide and oxygen. A thin film layer of basic zinc carbonate will be formed on the surface, which can delay the corrosion rate of zinc layer. The corrosion resistance of galvanized layer in aqueous solution of acid, alkali and sodium chloride is relatively strong. It is also not resistant to corrosion in atmospheres containing carbon dioxide and hydrogen sulfide and in Marine atmospheres; In high temperature and high humidity air and containing organic acid atmosphere is small, galvanized layer is also easy to be corroded.

The main customers of the thorn rope factory are still targeted at farms and plantations, because the demand for thorn rope is often very large.

1, stress relief before plating where the maximum tensile strength is greater than 1034Mpa key and important parts before plating should be at 200±10℃ stress relief for more than 1 hours, carburizing or surface quenching parts should be at 140±10℃ stress relief for more than 5 hours.

Cold galvanized, generally speaking, do not need heating, galvanized amount is little, this galvanized parts are easy to fall off in wet environment. Hot dip galvanizing, also known as hot dip galvanizing, is to melt the zinc ingot at high temperature, put some auxiliary materials in, and then dip the metal structural parts into the galvanized groove, so that the metal members are attached to a layer of zinc layer. The advantage of hot dip galvanized is that its anticorrosion ability is strong, the adhesion and hardness of galvanized layer is better.

Hot dip galvanizing, also known as hot dip galvanizing, is a method of obtaining a metal covering layer by immersing a steel member into a molten zinc solution. With the rapid development of high-voltage power transmission, transportation and communication, the protection requirements for steel parts are becoming higher and higher, and the demand for hot-dip galvanizing is also increasing. Usually the thickness of electrogalvanized layer is 5 ~ 15μm, and the large roll galvanized wire layer is generally more than 35μm, or even up to 200μm. Hot dip galvanized coating ability is good, dense coating, no organic inclusions.

Welding mesh is widely used in industry, agriculture, breeding, construction, transportation, mining and other aspects. Such as machine shields, animal fences, flower fences, window fences, access fences, poultry cages, egg baskets and home office food baskets, paper baskets and decorative. We can make it according to the special requirements of customers. Welding mesh is made of high quality low carbon steel wire row welding, and then cold plating (electroplating), hot plating, PVC plastic coated surface passivation, plasticizing treatment, smooth mesh, uniform mesh, solid solder joint, local machining stable performance, corrosion resistance, corrosion resistance. Features: Stainless steel mesh selection of high quality stainless steel wire row welding, more acid, alkali resistance, solid welding, beautiful, widely used and so on.

Heavy hexagonal mesh is made of steel wire woven into hexagonal mesh by special machinery. This kind of mesh, after cutting and assembling, can be made into fence mesh, mountain hanging mesh, vegetation three-dimensional mesh, assembly, etc. Alias: gabion mesh, heavy hexagonal mesh, ecological mesh, wire mesh, etc.