The iron is clean and clean, and then solvent treatment, after drying immersed in zinc liquid, iron and molten zinc reaction to produce an alloyed zinc layer, the process is: degreasing – washing – pickling – assisted plating – drying – hot dip galvanizing – separation – cooling passivation. The thickness of the alloy layer of hot plating wire mainly depends on the chemical composition of the steel silicon content, the size of the steel cross-sectional area, the roughness of the steel surface, the temperature of the zinc pot, the time of dipping zinc, cooling speed, cold rolling deformation, etc.

In moist air, a dense basic zinc carbonate film forms on the surface of zinc. Zinc coating belongs to the anodic coating, it is mainly used to prevent the corrosion of steel, its protective performance and the thickness of the coating is very important. The protective and decorative properties of zinc coating can be improved significantly after passivation treatment, dyeing or coating with light protection agent.

Cold galvanizing is also called electric galvanizing. It is the use of electrolytic equipment to remove oil, pickling, and then put the pipe into the solution of zinc salt, and connect the anode of the electrolytic equipment, place zinc plate on the opposite side of the pipe, and connect the positive pole of the electrolytic equipment to the power supply. A layer of zinc is deposited on the pipe fitting by directional movement of an electric current from the positive pole to the negative pole. Cold plated pipe fitting is processed before galvanizing.

The main customers of the thorn rope factory are still targeted at farms and plantations, because the demand for thorn rope is often very large.

After the corrosion of impregnated hexagonal wire mesh, the original characteristics will be lost, and the shape, color and mechanical properties will be changed, resulting in equipment damage, pipeline leakage, etc., specifically, it is easy to break and lose the original protection function. Usually, there are three kinds of metal corrosion: physical corrosion, chemical corrosion, electrochemical corrosion, corrosion in addition to the chemical properties and organizational structure of the metal itself, but also related to the surrounding medium, such as wet environment is easier to rust than dry environment, more impurities than impurities less easy corrosion, high temperature conditions than low temperature conditions easy corrosion. After understanding these, we can effectively prevent the corrosion of impregnated six-sided wire mesh, prolong the service life of the product.

Stainless steel barbed wire is often used in various engineering projects because of its good anti-corrosion ability, but it is difficult for ordinary families to accept because of its relatively high price. So what material of barbed rope anticorrosion ability is better?

Black iron wire application in the process, the main is through the hot metal billet rolling into six point five mm wire rod, and then put it in the drawing into a line of different diameter, the plant and then gradually narrow drawing plate aperture, cooling and annealing, plating process, such as making a variety of different specifications of the wire, the wire compared with ordinary black iron wire, will be more softer, Softness is also very uniform, color is also consistent, widely used in the construction industry, mining, chemical industry, welding mesh, welding coat hanger, reprocessing industry and so on.

1, no paint and maintenance, long new not old, exempt you from maintenance fatigue and trouble, the lowest comprehensive cost. Stainless steel wire mesh can be used as poultry cage, egg basket, channel fence, drain tank, porch guardrail, anti rat net, mechanical protective cover, livestock and plant fence, grid frame, etc.