In the process of composite electroplating galvanized wire, the plating solution must be stirred to obtain the composite coating in which the particles dispersed in the matrix metal. Stirring methods include mechanical stirring, air stirring, ultrasonic stirring, bath circulation, etc. The acid activation solution in the production process can remove the corrosion products and oxide film on the surface of the low carbon steel wire without excessive corrosion on the matrix.

Galvanizing is a process of coating a metal surface with zinc in an electrochemical reaction on the metal surface to improve the corrosion resistance of the metal. Wire drawing is a process in which metal materials are drawn by mechanical methods to reduce their cross-sectional area and increase their length. So, the combination of galvanized to wire drawing two processes, what impact on the performance of the product?

1, galvanized wire mesh molding sheet must be packed with flat hard data, to avoid eternal deformation due to poor packaging.

Zinc dipping time should be adjusted according to the thickness of wire diameter. The method of adjustment is to use the lead screw above the zinc pot, the length of the distance to the ceramic sinking roller. Thick wire diameter zinc dipping time should be long, fine wire diameter zinc dipping time should be short, zinc dipping length is in the range of 2~3.5m, which is also to reduce the zinc consumption of steel wire, is an aspect of maintaining the uniformity of zinc layer.

The production process of large coil galvanized wire is relatively simple. The wire after cleaning is put into electroplating solution first. Of course, the plating solution should contain zinc oxide, a direct current of steel, another zinc plate in the plating solution. The zinc is transferred to the surface of the steel as a molecule. If it shows a bright and beautiful color, the wire is coated with zinc.

Large roll galvanized wire is processed from high quality low carbon steel wire rod. Each wire rod rolled by continuous rolling mill is not less than 200kg, but 15% of the number of plates in each batch is allowed to be composed of two, of which the weight of each rod is not less than 80kg, and 4% of the number of plates in each batch is allowed, and the mass of its single wire rod is less than 200kg, but not less than 40kg. Each rod rolled by semicontinuous mill shall not be less than 60kg, and each batch shall be allowed to have 5% disk nitrogen. The mass of the rod shall not be less than 60kg, but not less than 30kg.

Hot dip galvanized wire is used in carbon structural steel, which is processed by drawing and hot dip galvanized. It is widely used in the manufacture of wire mesh, highway guardrail and construction projects. Electro galvanized wire is a kind of metal conforming material made of low carbon steel as core wire by wire drawing and electro galvanized process. Mainly used in wire mesh, highway guardrail and construction projects.