Hot wire is made of high quality low carbon steel, high carbon steel, after drawing, hot galvanized processing galvanized wire. Hot dip galvanized wire production process: wire rod – drawing – annealing – drawing – annealing – galvanized. Hot dip galvanized wire has the characteristics of thick coating, strong corrosion resistance and solid coating. And according to the special needs of users, according to the industry standard to provide various specifications of galvanized wire. Hot-dip galvanized wire is of better quality than electrodip galvanized wire. In the production process, hot dip galvanized wire has more than one annealing process, so the corrosion resistance of hot dip galvanized wire is stronger than that of electric galvanized wire.

Galvanizing is a process of coating a metal surface with zinc in an electrochemical reaction on the metal surface to improve the corrosion resistance of the metal. Wire drawing is a process in which metal materials are drawn by mechanical methods to reduce their cross-sectional area and increase their length. So, the combination of galvanized to wire drawing two processes, what impact on the performance of the product?

The production process of large rolls of galvanized wire is a level of drawing, through the mold into a slightly smaller diameter than the original. And so on down to the desired length. One pull is not desirable, must be numbered, from coarse to fine is dependent on metal ductility. If it changes too much it just breaks. After drawing to a certain diameter, galvanized, so that the finished product.

If the coating roughness is not caused by the above reasons, it may be caused by impurities in the plating solution. Can take a small amount of electroplating solution, after filtration test, then take a small amount of electroplating solution, after zinc powder treatment test, check the problem is caused by solid particles or copper, lead and other foreign metal impurities. Test them one by one and it’s not hard to find the cause of the problem. Galvanized iron wire coating foaming, binding force is not good.

The quality of hot-dip galvanized barbed wire is only the zinc layer attached to the surface of the wire, and with the chemical reaction, the zinc layer on the surface will gradually lose its role because of the oxidation reaction, which is more prominent in the humid environment. And because the use of rusty wire after all, it is said that the quality of hot-dip galvanized barbed wire is certainly not up to the level of stainless steel barbed wire.

There is still some demand for galvanized barbed rope by daily residents, but often the quantity is not particularly much. If the barbed rope factory delivers goods, then the extra freight may be higher than the price of the customer to buy the barbed rope in the market. The thorn rope factory sells to customers who buy in large quantities. There is a lot of demand for it, and it also hopes to find a manufacturer to purchase.

Hot dip galvanizing has been used for more than 150 years, and its principle has not changed so far. The steel structure should be fully immersed in zinc at one time to achieve uniform galvanized film structure. If it is too long or too wide to be dipped twice, the zinc layer at the joint will appear rough, too thick and so on. In addition, if the single weight of steel structure is too heavy, it will make its operation difficult if it exceeds the load of galvanizing equipment. Therefore, the communication with the hot dip galvanizing factory in advance.